Hardness, Brinell 137 Converted from Rockwell B, (500 kg load)
Hardness, Knoop 173 Converted from Rockwell B
Hardness, Rockwell A 51,1 Converted from Rockwell B
Hardness, Rockwell B 83
Hardness, Vickers 159 Converted from Rockwell B
Tensile Strength, Ultimate 536 MPa
Tensile Strength, Yield 454 MPa
Elongation at Break 20% in 50 mm
Modulus of Elasticity 125,5 GPa
Poisson's Ratio 0,36
Shear Modulus 46,4 GPa
Vanadium (Cold Rolled)
Hardness, Brinell 165 Converted from Vickers, (3000 kg load)
Hardness, Rockwell A 52 Converted from Vickers
Hardness, Rockwell B 100
Hardness, Rockwell C 3 Converted from Vickers, Value below normal HRC range, for comparison only
Hardness, Vickers 170
Tensile Strength, Ultimate 800 MPa
Tensile Strength, Yield 776 MPa
Elongation at Break 2% in 50 mm
Vanadium (Hot Rolled Bar)
Hardness, Brinell 142 Converted from Rockwell B, (500 kg load)
Hardness, Knoop 180 Converted from Rockwell B
Hardness, Rockwell A 52,3 Converted from Rockwell B
Hardness, Rockwell B 85
Hardness, Vickers 165 Converted from Rockwell B
Tensile Strength, Ultimate 472 MPa
Tensile Strength, Yield 439 MPa
Elongation at Break 27% in 50 mm
Vanadium (Vacuum Annealed Wire)
Hardness, Brinell 126 Converted from Rockwell A (500 kg load)
Hardness, Knoop 158 Converted from Rockwell A
Hardness, Rockwell A 48
Hardness, Rockwell B 78 Converted from Rockwell A
Hardness, Vickers 141 Converted from Rockwell A
Tensile Strength, Ultimate 538 MPa
Tensile Strength, Yield 463 MPa
Elongation at Break 25% in 50 mm
Vanadium (Cold Drawn Wire)
Hardness, Brinell 151 Converted from Rockwell A, (500 kg load)
Hardness, Knoop 192 Converted from Rockwell A
Hardness, Rockwell A 54
Hardness, Rockwell B 88 Converted from Rockwell A
Hardness, Vickers 176 Converted from Rockwell A
Tensile Strength, Ultimate 911 MPa
Tensile Strength, Yield 765 MPa
Elongation at Break 6,8% in 50 mm
Chromium (Annealed)
Hardness, Brinell 80 Converted from Vickers for 500 kg load/10 mm ball Brinell test
Hardness, Knoop 102 Converted from Vickers
Hardness, Rockwell B 48 Converted from Vickers
Hardness, Vickers 90
Charpy Impact, Unnotched 2 J (1,48 ft-lb) Unspecified Heat Treatment
Chromium (Recrystallized)
Tensile Strength, Ultimate 282 MPa
Elongation at Break 0%
Modulus of Elasticity 248 GPa
Chromium (As-Swaged)
Hardness, Brinell 125
Hardness, Knoop 144 Converted from Brinell
Hardness, Rockwell B 72 Converted from Brinell
Hardness, Vickers 131 Converted from Brinell
Tensile Strength, Ultimate 413 MPa
Tensile Strength, Yield 362 MPa
Elongation at Break 44%
Manganese
Hardness, Brinell 460 Converted from Vickers for 3000 kg load/10 mm ball Brinell test
Hardness, Rockwell A 75 Converted from Vickers
Hardness, Rockwell C 48 Converted from Vickers
Hardness, Vickers 500
Tensile Strength, Ultimate 496 MPa γ-Phase
Tensile Strength, Yield 241 MPa γ-Phase
Modulus of Elasticity 159 GPa
Bulk Modulus 92,6 GPa
Poisson's Ratio 0,35
Shear Modulus 76,4 GPa
Iron
Hardness, Brinell 146 Converted from Vickers for 3000 kg load/10 mm ball Brinell test
Hardness, Rockwell A 49
Hardness, Rockwell B 79
Hardness, Vickers 150
Tensile Strength, Yield 50 MPa 0,5% strain; after zone refining
Modulus of Elasticity 200 GPa
Bulk Modulus 166 GPa
Poisson's Ratio 0,291
Shear Modulus 87 GPa Calculated
Cobalt
Hardness, Brinell 125
Hardness, Vickers 253
Tensile Strength, Yield 225 MPa
Modulus of Elasticity 211 GPa
Poisson's Ratio 0,32
Shear Modulus 82,6 GPa
Nickel (Annealed)
Hardness, Vickers 75
Tensile Strength, Ultimate 45 MPa
Modulus of Elasticity 207 GPa
Poisson's Ratio 0,31
Shear Modulus 76 GPa
Nickel (Typical)
Tensile Strength, Ultimate 317 MPa
Tensile Strength, Yield 59 MPa
Elongation at Break 30%
Shear Modulus 76 GPa
Copper (Annealed)
Hardness, Vickers 50
Tensile Strength, Ultimate 210 MPa
Tensile Strength, Yield 33,3 MPa
Elongation at Break 60%
Modulus of Elasticity 110 GPa
Bulk Modulus 140 GPa
Poisson's Ratio 0,343
Shear Modulus 46 GPa
Copper (Cold-Worked)
Hardness, Brinell 89 Converted from Vickers for 500 kg load/10 mm ball Brinell test
Hardness, Rockwell A 35
Hardness, Rockwell B 51
Hardness, Vickers 100
Bulk Modulus 140 GPa
Poisson's Ratio 0,35
Copper (Cold Drawn)
Hardness, Rockwell B 37
Tensile Strength, Ultimate 344 MPa
Tensile Strength, Yield 333,4 MPa
Elongation at Break 14%
Bulk Modulus 140 GPa
Poisson's Ratio 0,364
Zinc
Hardness, Vickers 30
Tensile Strength, Ultimate 37 MPa cast sample
Modulus of Elasticity 96,5 GPa
Gallium
Hardness, Vickers 50
Germanium
Knoop Microhardness 7644 N/mm2
Modulus of Elasticity 130 GPa Average of three axes
Poisson's Ratio 0,3 Calculated
Shear Modulus 50 GPa Average of three axes
Selenium
Knoop Microhardness 350 N/mm2 Gray Selenium
Modulus of Elasticity 57,9 GPa
Shear Modulus 6,46 GPa
Rubidium
Modulus of Elasticity 2,35 GPa
Strontium
Bulk Modulus 11,61 GPa
Yttrium
Hardness, Vickers 40 highly anisotropic
Tensile Strength, Ultimate 150 MPa
Tensile Strength, Yield 67 MPa
Elongation at Break 34% in 25 mm
Modulus of Elasticity 63,5 GPa
Bulk Modulus 41,2 GPa
Poisson's Ratio 0,243
Shear Modulus 25,6 GPa
Zirconium
Hardness, Brinell 145 Converted from Vickers for 3000 kg load/10 mm ball, Annealed sample
Hardness, Rockwell A 49 annealed sample
Hardness, Rockwell B 78 Annealed sample
Hardness, Vickers 150 annealed sample
Tensile Strength, Ultimate 330 MPa Annealed
Tensile Strength, Yield 230 MPa Annealed
Elongation at Break 32% Annealed
Modulus of Elasticity 94,5 GPa
Poisson's Ratio 0,34
Shear Modulus 40 GPa Calculated